Liquid Glue Roof Chimney Sealant Paint Chimney Corrosion Resistant Coating

Name: Liquid Glue Roof Chimney Sealant Paint Chimney Corrosion Resistant Coating
Brand: Lianti
Price: 1 USD

Brand Name : Lianti

Model Number : KDW-116/KDW-982/KDW-987

Certification : ISO9001

Place of Origin : Jiangsu, China

MOQ : 1 Kilogram

Packaging Details : KDW-116: 10KG/iron drum; KDW-982: Component A: drum, 25KG/drum Component B: sausage, 0.4KG/sausage; plastic tube, 0.33KG/tube; KDW-987: 25KG/plastic drum

CAS No. : 63148-60-7

Other Names : anti-corrosion coating

EINECS No. : Unspecified

Classification : Other Adhesives

Main Raw Material : Silicone

Usage : chimney

Type : Liquid Glue

Color : White/Gray/Black

Application : Chimney

Appearance : Paste

Feature : Easy to spray

Packing : 25KG,10KG, etc

Certificate : ISO9001

Quality : Guarantee

Shelf life : 9 Months

Contact Now

Easy To Spray RTV Heat Resistant Silicone Adhesive Rubber For Chimney Anti-Corrosion Coating

Product Display

Liquid Glue Roof Chimney Sealant Paint Chimney Corrosion Resistant Coating

Product Description

Detailed Images

Key performance indicators of KDW-116
Item	Units of measurement	Performance	Test method
Adhesive strength	Mpa	≥1	GB/T 16777
Temperature resistance	℃	≥180	GB/T 16777
Completely curing time	h	≥180	GB/T 16777

Key performance indicators of KDW-982
Item		Unused		Used	Test method
		A	B
Uncured	Appearance & color	White/gray paste	Black paste	Black	Visual
	Density(g/cm³)	1.3~1.5	1.08	1.3~1.5	GB/T13477.2
Operation time (h)		1~2			-
Curing time (25℃, h)		24~48			-
Cured	Tensile strength (Mpa)	≥2.0			GBT/528 Dumbbell I type, 500mm/min
	Elongation (%)	≥100			GBT/528 Dumbbell I type, 500mm/min
	Shore hardness	40~60			GBT/531
	Shear strength (Mpa)	≥1.5			GBT/7124 5mm/min, steel to steel
	50℃, 5% vitriol soak for 7 days (%)	No significant change on appearance, retention rate of tensile strength ≥80			GBT/528 Dumbbell I type, 500mm/min
	Heat resistance (180℃, 24h)	No significant change on appearance, retention rate of tensile strength ≥80			GBT/528 Dumbbell I type, 500mm/min
	80℃, 7 days, acid corrosion resistance to the mixture composed of 2% vitriol, 0.1% hydrochloric acid, 0.1% nitric acid and 0.1% phosphoric acid (%)	No significant change on appearance, retention rate of tensile strength ≥65			GBT/528 Dumbbell I type, 500mm/min

	Adhesive strength (steel to steel) (Mpa)	≥1.0			GB/T50212

Key performance indicators of KDW-987
Item		Performance	Test methods
Uncured	Appearance & color	Black paste	Visual
	Density (g/cm³)	1.2~1.4	GB/T13477.2
	Tack free time (min)	10~30	Touch method
	Tensile strength (Mpa)	≥2.0	GB/T 528 Dumbbell I type, 500mm/min
	Elongation (%)	≥200	GB/T 528 Dumbbell I type, 500mm/min
	Shore hardness (A)	30~50	GB/T 531
	Shear strength (Mpa)	≥1.5	GB/T 7124 5mm/min, steel to steel
	80℃, 20% vitriol soak for 7 days (%)	No significant change on appearance, retention rate of tensile strength ≥65	GB/T 528 Dumbbell I type, 500mm/min
	Heat resistance (180℃, 48h)	No significant change on appearance, retention rate of tensile strength ≥90	GB/T 528 Dumbbell I type, 500mm/min
	80℃, 14 days, acid corrosion resistance to the mixture composed of 2% vitriol, 0.1% hydrochloric acid, 0.1% nitric acid and 0.1% phosphoric acid (%)	No significant change on appearance, retention rate of tensile strength ≥70	GB/T 528 Dumbbell I type, 500mm/min
	Adhesive strength (steel to steel) (Mpa)	≥1.0	GB/T 50212

Packing & Delivery

Packing.

1. KDW-116:10KG/iron drum;

2. KDW-982:

Component A: drum, 25KG/drum

Component B: sausage, 0.4KG/sausage;

plastic tube, 0.33KG/tube;

3. KDW-987: 25KG/plastic drum.

Storage and transportation.

Stored in the sealed containers, the temperature should not be higher than 28℃, and the shelf life would be 9 months in sealed at 23~25℃..

Operation process.

1. KDW-116 (Prime coating):
1) Clean the surface:
Clean the surface of chimney inner wall as general surface, remove dust and greasy dirt.
2) Sizing:
Take the prime coating out of the package, spray it on the surface of chimney inner wall with professional spraying tools, and just dried at room temperature.

2. KDW-982 (Chimney anti-corrosion masonry rubber):
1) Mix rubber:
The recommended ratio is 10:1(component A: component B), and the operation time would be 1 hour when the operation temperature is 25℃. Increasing or decreasing the amount of component B within ±15% to speed up or slow down the curing speed.
2) Stir:
Completely stir the rubber with electric tool or other stirrer, the mixed rubber should be black, if it is white or too shallow, or local color is too deep, it is needed to stir until evenly colored.
3) Paste:
Evenly smear the mixed chimney anti-corrosion rubber on foam glass bricks or light vitreous tiles, ensure that the thickness of rubber between bricks and chimney inner wall is not less than 3mm and the thickness between bricks is not less than 1mm.

3. KDW-987 (Chimney anti-corrosion interface rubber):
1) Clean the surface:
Clean the surface of chimney inner wall as general surface, remove dust and greasy dirt.
2) Sizing:
Take the rubber out of package, smear smoothly the rubber on the surface of chimney inner wall with professional tools, let it cured at room temperature.
3) Cure:

The product is cured at room temperature, and it is solidified into elastomer by absorbing moisture in the air, whether completely cured depends on the thickness. (2~3mm thickness, at 25℃, humidity of 50%, it could be completely cured within 24 hours).